Mild Steel Plates
Mild Steel (MS) Plates are a versatile and cost-effective solution for a wide range of industrial and structural applications. Derived from carbon steel with a low-carbon alloy composition, these plates offer superior weldability, ductility, and machinability compared to higher carbon alternatives. Jitu Milan Steels supplies MS plates in various finishes, including hot-rolled, cold-rolled, and polished options, to suit your specific project requirements.
Our MS plates are highly valued by clients for their exceptional tensile strength, rugged design, and long-term durability. Because they are easy to form and weld, they are widely used in the manufacturing of furniture, window frames, stair rails, and general structural components. We utilize high-quality raw materials and modern techniques to ensure all products meet rigorous specifications while remaining the most affordable choice for high-volume projects.
Mild Steel Plates Other Types
| ASTM (USA) | IS (INDIA) | DIN (GERMANY) | EN (EUROPE) | JIS (JAPAN) |
| A 36 | IS 2062: E250 Gr A/ B/ C | DIN 17100: ST 37.3, ST 44.2, ST 44.3 | EN 10025: S235, S275 | G 3106: SM400 |
| A 283: A, B, C, D | G 3101: SS400 |
We deal in all Length is from 5MM to 700MM as per client's requirements.
Mild Steel Plate Grades
- IS 2062 E250
- A283 GR.C
- IS 2062 FE 410
- SS400
- ASTM A36
- S275 JR
- IS 2062 GR A /B
Specifications
Thickness : 5mm-150mm
Width : 1000mm – 4500mm
Length : 5000mm – 1500mm
Process : Hot-Rolled (HR)
| Grade | C% | Mn% | P% | S% | Si% | Al% | CE |
| IS 2062 E250BR | 0.1500 | 0.8100 | 0.0190 | 0.0210 | 0.0900 | 0.0360 | 0.2850 |
| 0.1500 | 0.7600 | 0.0150 | 0.0160 | 0.1110 | 0.0300 | 0.2770 | |
| 0.1400 | 0.8000 | 0.0230 | 0.0120 | 0.0120 | 0.0380 | 0.2730 |
| Grade | С | Si | Mn* | S | P | Cu** |
| ASTM A36 | ≤ 0.25 | ≤ 0.40 | ~ | ≤ 0.05 | ≤ 0.04 | ≥ 0.20 |
| Grade | C | Mn | P | S | Si | Cu |
| ASTM A283 Gr.C | 0.24 | 0.90 | 0.035 | 0.04 | 0.40 0.15-0.40 | 0.20 |
| Grade | C | Mn | P | S | N | Cu | CEV |
| S275 JR | 0.22 max. | 1.5 max. | 0.04 max. | 0.04 max. | 0.012 max. | 0.55 max. | 0.42 max. |
| Grade | C | Mn | Su | Ph |
| IS 2062 Fe 410 | 0.23 max. | 1.50 max. | 0.045 max. | 0.045 max. |
| Grade | C | Mn | S | P | Si |
| IS 2062 GR.B | 0.22 | 1.5 | 0.045 | 0.045 | 0.4 |
| Grade | Fe | Si | C | S | P | |
| SS400 | min. | 99.25 | – | – | – | – |
| max. | 100 | 0.4 | 0.26 | 0.050 | 0.040 | |
| Grade | Yield strength N/mm2 | Tensile strength N/mm2 | Elongation (%) |
| IS 2062 E250 | 250 min | 410 min | 23 |
| Grade | Yield strength, MPa (min) | Tensile strength, MPa | Elongation(sample 200 mm),% (min) |
| ASTM A36 | 250 | 400-550 | 20 |
| Grade | Tensile strength | Yield strength, min, [MPa] | Elongation in 2″ | Elongation in 8″ |
| A283 GR.C | 55,000 75,000 psi [380 – 515 MPa] | 30,000psi [205 MPa] | 25% min | 22% min |
| Grade | Tensile strength, Rm, MPa (N/mm2) | 0,2% Yield strength, Rp0, 2min, (MPa) | Brinell hardness, HB max |
| S275 JR | 380-540 | 275 | 121 – 163 |
| Grade | Yield Rp0.2 (MPa) | Tensile Rm (MPa) | Impact KV/Ku (J) | Elongation A (%) | Reduction in cross section on fracture Z (%) | As-Heat-Treated Condition | Brinell hardness (HBW) |
| IS 2062 FE 410 | 864 (≥) | 434 (≥) | 41 | 23 | 12 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 422 |
| Grade | Yield strengtd (Mpa)(Min) | Tensile strengtd (Mpa)(Min) | Elongation (%) | IMPACT (Min) | ||
| ＜20mm | 20mm-40mm | ＞40mm | ||||
| IS 2062 GR A/B | 250 | 240 | 230 | 410 | 23 | 27J at 0 ° C |
| Grade | Yield Strength min. (Mpa) | Tensile Strength (Mpa) | Elongation min. % | ImpactResistancemin.[J] | |||
| Thickness ＜16 mm | Thickness ≥16mm | Thickness | Thickness | Thickness | |||
| ＜5mm | 5-16mm | ≥16mm | |||||
| SS400 | 245 | 235 | 400-510 | 21 | 17 | 21 | – |